Quote:
Originally Posted by capesams
I think we all agree 316 is the longest lasting,,best wire...But it's a bitch to work with if using plyer's by hand....now back to the annealed wire...there has to be something between soft and rock hard 316,,,where's the middle ground here??
|
I don't think you can temper 316, so cold worked would be as hard as 316 gets. I'm no metalurgist, but the annealed wire has to cold work to some extent just by twisting it. Maybe someone could shed some light on that.
You know . . . you could just use titanium.