04-25-2014, 06:53 PM
|
#1
|
Big E
Join Date: Dec 2009
Location: Seabrook, NH
Posts: 681
|
Sealing Test Results for Yellow Birch
This is a test of the effectiveness of four sealers applied to yellow birch lures. The sealers are: - ESP 155 epoxy(*)
- 75% Low V epoxy(**)/25% acetone
- 60% Helmsman (***)/40% mineral spirits
- 50% Tung oil/33% turpentine/17% Helmsman (***)
(*) ESP 155 is a commercial penetrating epoxy containing 24% Xylene
(**) Low V is a low viscosity epoxy consisting of 100% solids
(***) Minwax Helmsman spar urethane, satin sheen, quart-can
I chose these four sealers to test because they were products I collected over the past few years but I never compared them objectively.
Last edited by Eric Roach; 04-25-2014 at 07:08 PM..
|
|
|
|
04-25-2014, 06:54 PM
|
#2
|
Big E
Join Date: Dec 2009
Location: Seabrook, NH
Posts: 681
|
Point of Testing
Specifically, I wanted to look at the following (in order of interest): - See which sealer best protects lures from punctures in the surface of the wood
- See which sealer best protects undamaged lures
- Compare drying times of sealers
- Compare cost of sealers
|
|
|
|
04-25-2014, 06:59 PM
|
#3
|
Big E
Join Date: Dec 2009
Location: Seabrook, NH
Posts: 681
|
Lures Used in Testing
Some info about the lures created for the test: - Turned from same piece of yellow birch lumber
- Turned to same dimensions on Vega (.9” width, 4.5” length, rear taper to .375”)
- 90° cut on face
- Through-drilled with 7mm belly hook hole
- Average lure weight: .993 oz
- 33 lures were turned:
- 3 were left raw (not sealed or painted)
- 6 were left unsealed but primed and painted (3 were punctured, 3 were left undamaged)
- 6 were sealed with ESP 155 (3 were punctured, 3 were left undamaged)
- 6 were sealed with Low V acetone (3 were punctured, 3 were left undamaged)
- 6 were sealed with Helmsman/mineral spirits (3 were punctured, 3 were left undamaged)
- 6 were sealed with tung/turpentine/Helmsman (3 were punctured, 3 were left undamaged)
- Because my main interest was seeing how well the sealers protected against punctures, I primed & painted the lures to be a little more realistic about the additional water-impermeable layers we put on real lures. Priming & painting consisted of:
- 2 coats of 50% Zinsser Cover Stain/50% naphtha dip-primer
- 1 coat of Valspar spray primer
- 1 coat of Valspar spray lacquer
- Half of the lures were punctured after sealing/priming/painting to simulate bluefish teeth and hook point damage. Each lure that was punctured received 8 identical holes from the very tips of #15 twist nails at a depth of ~ 3/32”; a jig was used to place holes in the same locations on each punctured lure.
|
|
|
|
04-25-2014, 07:00 PM
|
#4
|
Big E
Join Date: Dec 2009
Location: Seabrook, NH
Posts: 681
|
Sealer Application
See attached for info about how sealers were applied and how much weight they gained immediately after sealing.
|
|
|
|
04-25-2014, 07:02 PM
|
#5
|
Big E
Join Date: Dec 2009
Location: Seabrook, NH
Posts: 681
|
Sealer Drying Data
- Data based on average of 6 lures per sealer
- Lures were hung in basement in conditions that averaged 70 degrees / 50% humidity
- Attached table shows weight increase of lures after sealer dried (ounces, grams and percent of pre-sealed weight)
- Attached chart shows decrease in lure weights (in percent) over time as solvent evaporated
|
|
|
|
04-25-2014, 07:03 PM
|
#6
|
Big E
Join Date: Dec 2009
Location: Seabrook, NH
Posts: 681
|
Immersion Testing
After puncturing half of the lures, they were placed in an eel bag and submerged in saltwater. They were removed at time intervals to be blown out with compressed air and weighed on a lab balance to record the amount of weight gained by water absorption. It took an average of 20 minutes to weigh all lures and submerge them again. The time interval for the next weigh-in began when they were returned to the water. The posts below contain both data tables and graphs. Graphs are all based on percentage of lure weight gained over time. Each value represents an average of three lures.
|
|
|
|
04-25-2014, 07:05 PM
|
#7
|
Big E
Join Date: Dec 2009
Location: Seabrook, NH
Posts: 681
|
Water Gain of Punctured Lures
(This was the testing I was most interested in) - Attached summary table shows increase in lure weight (in ounces, grams and percent of original weight) over time for PUNCTURED lures
- Attached chart shows increase in lure weight (in percent of original weight) over time for PUNCTURED lures
|
|
|
|
04-25-2014, 07:06 PM
|
#8
|
Big E
Join Date: Dec 2009
Location: Seabrook, NH
Posts: 681
|
Water Gain of Undamaged Lures
- Attached summary table shows increase in lure weight (in ounces, grams and percent of original weight) over time for UNDAMAGED lures
- Attached chart shows increase in lure weight (in percent of original weight) over time for UNDAMAGED lures
|
|
|
|
04-25-2014, 07:06 PM
|
#9
|
Big E
Join Date: Dec 2009
Location: Seabrook, NH
Posts: 681
|
Sealer Cost Comparison
The attached table is a comparison of the costs associated with each of the four sealers, as well as the dip-primer I use. Costs are compared by $/ounce, $/cup, and $ to initially buy components if you needed all the components. NOTE that the costs associated by volume for epoxy-based sealers are for one-time usage. This greatly increases their overall cost of use.
|
|
|
|
04-25-2014, 07:07 PM
|
#10
|
Big E
Join Date: Dec 2009
Location: Seabrook, NH
Posts: 681
|
Thoughts About the Testing
- I was primarily interested in seeing how well the sealers performed over a 6 hour period, which is about the longest I can wetsuit at a stretch these days.
- The difference in the performance of the sealers (as a part of the system) was negligible to my mind – both for punctured and undamaged blanks. The tables do the best job of showing how close they are -- the charts had to be magnified in order to better show the visual separation.
- I have been using ESP-155. My assumption that this solvent-thinned epoxy protected punctured lures better than oil-based or urethane-based sealers isn’t appreciably true.
- With such similar performance, it’s easier for me to give more consideration to other factors. Epoxy sealing is greatly more expensive, so I will not be replacing it when I run out.
- I did not do a breakdown of safety-related issues with each sealer, as I didn’t feel qualified to say anything other than what has been said in other threads: Xylene/xylol and acetone should be left out of hobby plug building. It’s going to be much easier leaving this behind after this test.
- I will move on to sealing with the tung oil solution, primarily because I have an 80 oz jar of it, and it has held up to storage quite well (it wasn’t touched for 18 months prior to this test, and it had only a very light skim on it.)
A lot of work, but I’m glad I did it. Hope this helps someone else out.
Eric
|
|
|
|
04-26-2014, 04:44 AM
|
#11
|
Oblivious // Grunt, Grunt Master
Join Date: Nov 2005
Location: over the hill
Posts: 6,682
|
That was informative and fun, thanks.
|
|
|
|
04-26-2014, 07:24 AM
|
#12
|
Registered User
Join Date: Jul 2004
Location: Buxton, Maine
Posts: 1,727
|
Thanks Eric. that was a load of work and some great info.
|
|
|
|
04-26-2014, 08:21 AM
|
#13
|
Registered User
Join Date: Feb 2012
Location: Middleboro
Posts: 43
|
Thank you Big E, for a hobbiest like me, your indepth study really take the guess work out of sealing. It was an area that had very little available info to include weight gains and cost effectiveness. Great study, thanks again for sharing that info.
|
|
|
|
04-27-2014, 07:34 AM
|
#14
|
Registered User
Join Date: Nov 2004
Location: plymouth,ma
Posts: 1,142
|
That was interesting especially when it gets to the cost of the various methods. Every year I seem to do a little less building so have been trying to keep the costs down. I have messed around with using the different epoxies that I had been using as top coats as sealers and i have not noticed any appreciable difference between any of them.
I do like how the epoxies harden the wood. Some epoxies like Etex are a lot cheaper than others like the sys 3 products and when thinned with denatured alchohol they seem to work just as well as a sealer. Nice thing is I can use the same product for sealing and topcoat, and shelf life does not seem to be an issue.
|
|
|
|
04-27-2014, 07:53 AM
|
#15
|
Registered User
Join Date: Jan 2010
Location: S. Easton
Posts: 1,676
|
Great breakdown Eric!!! Very scientific!
|
"Always two there are, no more, no less: a master and an apprentice." >> Yoda
|
|
|
04-29-2014, 06:42 AM
|
#16
|
Registered User
Join Date: Aug 2005
Location: the Dirty Jerz
Posts: 276
|
Eric,
Great job and thank you for sharing the results. Remember what ever we do to seal, paint, look pretty, etc. The goal should always be to have a warrior that gets beat to hell and looks like the following.
Nothing makes me happier than to see my lures beat to hell like this with chunks missing and still fishing well.
Billy
|
|
|
|
06-02-2014, 10:06 PM
|
#17
|
Pluggin' Addict
Join Date: Dec 2004
Location: Knee deep in the hoopla
Posts: 54
|
Nice work! With the urethane or tung oil mixes you can always do a second dip for added protection. First dip might not close all the pores
Posted from my iPhone/Mobile device
|
|
|
|
01-27-2015, 10:48 AM
|
#18
|
Registered User
Join Date: Oct 2005
Posts: 2,038
|
Very impressive Eric!
Would love to see this done with the other woods used for plugs: AYC, WRC, EWC, pine, etc..
If you do maybe you could take up a collection so that everyone who benefits shares in the expense? I would gladly pitch in.
|
|
|
|
|
Thread Tools |
|
Display Modes |
Rate This Thread |
Linear Mode
|
|
Posting Rules
|
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts
HTML code is Off
|
|
|
All times are GMT -5. The time now is 06:39 PM.
|
| |